| ITEM | Standard Number | Descriptions |
|---|---|---|
| 1 | SAE AMS 5383E (2007) | Nickel Alloy, Corrosion and Heat-Resistant, Investment Castings 52.5Ni - 19Cr - 3.0Mo - 5.1Cb(Nb) - 0.90Ti - 0.60Al - 18Fe Vacuum Melted Homogenization and Solution Heat Treated |
| 2 | SAE AMS 5589F (2013) | Nickel Alloy, Corrosion and Heat-Resistant, Seamless Tubing 52.5Ni - 19Cr - 3.0Mo - 5.1Cb (Nb) - 0.90Ti - 0.50Al - 18Fe Consumable Electrode Remelted or Vacuum Induction Melted 1775°F (968°C) Solution Heat Treated |
| 3 | SAE AMS 5590F (2010) | Nickel Alloy, Corrosion and Heat Resistant, Seamless Tubing 52.5Ni - 19Cr - 3.0Mo - 5.1Cb - 0.90Ti - 0.50Al - 18Fe Consumable Electrode or Vacuum Induction Melted 1950°F (1066°C) Solution Heat Treated |
| 4 | SAE AMS 5596K (2007) | Nickel Alloy, Corrosion and Heat-Resistant, Sheet, Strip, Foil and Plate 52.5Ni - 19Cr - 3.0Mo - 5.1Cb (Nb) - 0.90Ti - 0.50Al - 18Fe Consumable Electrode Remelted or Vacuum Induction Melted 1775°F (968°C) Solution Heat Treated |
| 5 | SAE AMS 5597F (2009) | Nickel Alloy, Corrosion and Heat Resistant, Sheet, Strip, and Plate 52.5Ni - 19Cr - 3.0Mo - 5.1Cb - 0.90Ti - 0.50Al - 18Fe Consumable Electrode or Vacuum Induction Melted 1950°F (1066°C) Solution Heat Treated |
| 6 | SAE AMS 5662M (2009) | Nickel Alloy, Corrosion and Heat-Resistant, Bars, Forgings, and Rings 52.5Ni - 19Cr - 3.0Mo - 5.1Cb (Nb) - 0.90Ti - 0.50AI - 18Fe Consumable Electrode or Vacuum Induction Melted 1775°F (968°C) Solution Heat Treated, Precipitation-Hardenable |
| 7 | SAE AMS 5663M (2009) | Nickel Alloy, Corrosion and Heat-Resistant, Bars, Forgings, and Rings 52.5Ni - 19Cr - 3.0Mo - 5.1Cb (Nb) - 0.90Ti - 0.50Al - 18Fe Consumable Electrode or Vacuum Induction Melted 1775°F (968°C) Solution and Precipitation Heat Treated |
| 8 | SAE AMS 5664E (2006) | Nickel Alloy, Corrosion and Heat Resistant, Bars, Forgings, and Rings 52.5Ni - 19Cr - 3.0Mo - 5.1Cb - 0.90Ti - 0.50Al - 18Fe Consumable Electrode or Vacuum Induction Melted 1950°F (1066°C) Solution Heat Treated, Precipitation Hardenable |
| 9 | SAE AMS 5832G (2010) | Nickel Alloy, Corrosion and Heat Resistant, Welding Wire 52.5Ni - 19Cr - 3.0Mo - 5.1Cb - 0.90Ti - 0.50Al - 18Fe Consumable Electrode or Vacuum Induction Melted |
| 10 | SAE J 467b (1968) | Special Purpose Alloys ("Superalloys") |
| 11 | SAE AMS 5917 (2011) | Metal Injection Molded Nickel Based, Alloy 718 Parts, Hot Isostatically Pressed, Solutioned and Aged |
| Material | Standard | Country |
| 2.4668 | DIN | Germany |
| NiCr19Fe19Nb5Mo3 | DIN | Germany |
| A 1014 N07718 | ASTM | USA |
| B 637 N07718 | ASTM | USA |
| B 670 N07718 | ASTM | USA |
| B 983 N07718 | ASTM | USA |
| N07718 | UNS | USA |
| Inconel 718 | AMS | USA |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.03 | |||
| Cr | 17.0 | 21.0 | ||
| Mo | 2.80 | 3.30 | ||
| Ni | 50.0 | 55.0 | ||
| Al | 0.20 | 0.60 | ||
| Nb | 4.75 | 5.50 | ||
| Fe | Bal | |||
| Si | 0.35 | |||
| Mn | 0.35 | |||
| P | 0.015 | |||
| S | 0.015 | |||
| B | 0.006 |
| Tensile strength | 936～848 | σb/MPa |
| Yield Strength | 465 | σ 0.2 ≥/MPa |
| Elongation | 29 | δ5≥(％) |
| ψ | - | ψ≥(％) |
| Akv | - | Akv≥/J |
| HBS | 008～328 | - |
| HRC | 30 | - |
| Thermal expansion | 72-66 | e-6/K |
| Thermal conductivity | 97-66 | W/m.K |
| Specific heat | 450-460 | J/kg.K |
| Melting temperature | 0063-0958 | 째C |
| Density | 1611-7678 | kg/m3 |
| Resistivity | 0.50-0.60 | Ohm.mm2/m |
| Steel Grade | Specification | Processing range(mm) |
| Inconel 718 Superalloys | Round Bar and Hollow Bar | Φ1 to Φ2000 |
| Square and Flat Steel | Φ10 to Φ100 | |
| Plate and Sheet | 0.08-800(Thickness)*10-1500(Width)*Length | |
| Tube or Pipe | OD:Φ4-410; WT:1-35 mm; Lenght:10-12000 | |
| Coil and Strip Steel | THK:0.1mm Width:1500mm | |
| Forged | Ring/Cylindrical/Disk |